The present invention relates to a method for manufacturing semiconductor fluorescent nanoparticles to be applied to optics and displays and, more specifically, comprises the steps of: making a mixed solution by mixing a first precursor material into a first coordinating solvent contained in a reaction container and stirring the same; heating the mixed solution at a synthesis temperature while stirring the mixed solution; making a synthesized solution by mixing, at the synthesis temperature, an additional solution, in which a second precursor material is mixed into a second coordinating solution, and the mixed solution so as to form nuclei during a synthesis time; and quenching the synthesized solution to a set temperature at a set cooling speed after the synthesis time expires.
본 발명은, 광학 및 디스플레이 응용을 위한 반도체 형광나노입자의 제조방법에 관한 것으로, 보다 상세하게는, 제1전구물질을 반응용기에 담겨진 제1배위용매에 혼합한 후 교반하여 혼합용액을 만드는 단계와; 상기 혼합용액을 교반하면서 합성온도로 가열하는 단계와; 상기 합성온도에서 제2전구물질을 제2배위용매에 혼합한 첨가용액을 상기 혼합용액과 혼합하여 합성시간동안 핵을 형성하여 합성용액을 만드는 단계와; 상기 합성시간이 경과한 후, 상기 합성용액을 설정된 냉각속도로 설정온도까지 급냉하는 단계;를 포함하는 것을 요지로 한다.patents-wipo patents-wipo