In the ultraviolet irradiation step, the illuminance of the vacuum ultraviolet light received by the coating film on the coating film surface is not more than 160 mW/cm2, and the amount of energy of the vacuum ultraviolet light on the coating film surface received during an interval (T), in which the illuminance of the vacuum ultraviolet light on the coating film surface is between 50 mW/cm2 and 160 mW/cm2, is between 180 mJ/cm2 and 1800 mJ/cm2.
French[fr]
Dans l'étape d'irradiation aux ultraviolets, l'éclairage de la lumière ultraviolette du vide reçu par la pellicule protectrice sur la surface de pellicule protectrice n'est pas supérieur à 160 mW/cm2, et la quantité d'énergie de la lumière ultraviolette du vide sur la surface de pellicule protectrice reçue pendant un intervalle (T), dans lequel l'éclairage de la lumière ultraviolette du vide sur la surface de pellicule protectrice est entre 50 mW/cm2 et 160 mW/cm2, est entre 180 mJ/cm2 et 1800 mJ/cm2.
Japanese[ja]
本発明は、基材上にポリシラザン化合物を含有する塗布液を塗布して塗膜を形成する塗布工程および、基材を光源に対して相対的に移動させ、真空紫外線を塗膜に照射して、ガスバリア性層を形成する紫外線照射工程を有し、紫外線照射工程において、塗膜が受ける塗膜面での真空紫外線の照度は160mW/cm2以下であり、塗膜面での真空紫外線の照度が50mW/cm2以上、160mW/cm2以下である期間Tを有し、期間T内に受ける、塗膜面における真空紫外線のエネルギー量が、180mJ/cm2以上1800mJ/cm2以下であるガスバリアフィルムの製造方法であり、ロール・トゥー・ロール方式の生産適性を有し、生産性に優れ、ガスバリア性能に優れるガスバリアフィルムを製造することができるガスバリアフィルムの製造方法が提供できる。